SPARKMIX EPOXY CBE (Concrete Bonding Epoxy)
Conforms to ASTM C-881-90 Type I, II, III, IV, V Grade 2, Class B & C
A two-component, solvent free, high viscosity epoxy system that is ideal for bonding “old” and “new” concrete. It is an all purpose bonding epoxy that is good for repairing when a non-sagging material is required.
SPARKMIX EPOXY CBE is best used in repairing concrete scaling.
Compressive Strength : Standard CBE
5,500 psi (minimum), 1 day @ field temperature
8,500 psi (minimum), 7 days @ field temperature
Compressive Strength : CBE-HS (High Strength)
5,500 psi (minimum), 1 day @ field temperature
10,000 psi (minimum), 7 days @ field temperature
SPARKMIX EPOXY IE (Injection Epoxy)
Conforms to ASTM C-881-90 Type I, III, IV Grade 1, Class C
A two-component, solvent free, low viscosity epoxy system that is best for grouting and repairing damaged concrete. As injection epoxy, it can penetrate tiny cracks with the used of pressurized epoxy injection machine and commonly used in repairing horizontal, vertical and overhead cracks when conventional repair method is not sufficient.
Compressive Strength : 10,000 psi (minimum)
Compressive Modulus : 380,000 psi
SPARKMIX EPOXY GE (Grouting Epoxy)
Conforms to ASTM C-881-90 Type I, III, IV Grade 1, Class C
A three-component, solvent free,low viscosity epoxy system that is good for grouting and repairing damaged concrete such as honeycombs. Mixed with silica sand aggregate produces workable sag resistant mortar for overhead or vertical patching. non-sag consistency makes material suitable for horizontal or overhead embedment of dowel, bolts and other anchors.
Compressive Strength :
1 : 1 Ratio of Epoxy to Silica Sand
8,000 psi (minimum), 1 day
11,000 psi (minimum), 7 days
1 : 1.5 Ratio of Epoxy to Silica Sand
7,500 psi (minimum), 1 day
10,000 psi (minimum), 7 days
1 : 2 Ratio of Epoxy to Silica Sand
7,000 psi (minimum), 1 day
10,000 psi (minimum), 7 days
1 : 2.5 Ratio of Epoxy to Silica Sand
6,500 psi (minimum), 1 day
9,000 psi (minimum), 7 days
SPARKMIX EPOXY PDE (Rapid Curing, Pile Splicing Epoxy)
Conforms to FED, SPEC. MMM-A-001993
A two-component, low viscosity, rapid cure, chemical resistant epoxy with high physical strength. It is 100% solid epoxy that uses polymeric amino amine curing agent. SPARKMIX EPOXY PDE is specifically formulated for use in rapid setting application like pile splicing, cable splicing and numerous small casting applications where exothermic temperature rise is not prohibited.
It can be used to secure anchor bolts, rebars and dowels into concrete. To build up the epoxy adhesive, 20 to 30 mesh dry silica sand should be added to the mixed epoxy.
SPARKMIX EPOXY FGE (Food Grade, Tank Lining Epoxy)
A two-component, solventless, non-toxic in cured state, chemical resistant epoxy with high physical strength. it is 100% solid epoxy that uses modified polyamide resin as curing agent. SPARKMIX EPOXY FGE is specifically formulated food grade epoxy for use in tank lining applications, including the lining of tanks made of concrete or metal that will be used to contain potable water, wines, beer, vinegar and vegetable oils.
SPARKMIX EPOXY NSE (General Purpose, Non-Sag Epoxy Adhesive)
A specially formulated general purpose, non-sag epoxy adhesive. This product is of two components, solventless, paste consistency and cures at room temperature. When the two components (Resin + Hardener) are mixed and cure, the result is a thermosetting material that is unaffected by water, acid, alkalis, fuel oil, hot gases and other organic solvents.
SPARKMIX EPOXY ME (Marine Epoxy)
A specially formulated marine epoxy primarily used for the construction and repair of wooden boats. it has good adhesion to wooden surfaces as well as to metal and even plastic surfaces. This product is of two components, filled type and cures at room temperature. When two components (Resin + Hardener) are mixed and cured, the result is a tough and resilient thermosetting material which make it very suitable for rot prevention and repair of all kinds of wooden boats as well as coating, encapsulating the wooden parts of boat against rot.
SPARKMIX EPOXY PJE (Pipe Jointing Epoxy)
A specially formulated pipe jointing epoxy adhesive. This product is of two components, filled type, heavy paste consistency and cures at room temperature. When the two components are mixed and cured, the result is a thermosetting material that is unaffected by water, acids, alkalis, fuel oil, hot gases and other organic solvents.
SPARKMIX EPOXY UW (Underwater Epoxy)
A two-component, solvent free, 100% solid epoxy system. A medium viscosity epoxy specially formulated that is good for bonding and repairing concrete and other irregular objects under water or under wet or damp conditions. After mixing the two components, the result is a medium viscosity epoxy mix that will cure even at low temperature.